Shape-memory polymer

Shape-memory polymers (SMPs)are polymericsmart materialsthat have the ability to return from a deformed state (temporary shape) to their original (permanent) shape when induced by an external stimulus (trigger), such as temperature change.[1]

IUPACdefinition

Polymer that, after heating and being subjected to a plastic deformation, resumes its original shape when heated above its glass-transition or melting temperature[2]

Note:

  • Crystalline trans-polyisoprene is an example of a shape-memory polymer.

Properties of shape-memory polymers

edit

SMPs can retain two or sometimes three shapes, and the transition between those is often induced by temperature change. In addition to temperature change, the shape change of SMPs can also be triggered by an electric ormagnetic field,[3]light[4]or solution.[5]Like polymers in general, SMPs cover a wide range of properties from stable tobiodegradable,from soft to hard, and from elastic to rigid, depending on the structural units that constitute the SMP. SMPs includethermoplasticandthermoset(covalently cross-linked) polymeric materials. SMPs are known to be able to store up to three different shapes in memory.[6]SMPs have demonstrated recoverable strains of above 800%.[7]

Two important quantities that are used to describe shape-memory effects are the strain recovery rate (Rr) and strain fixity rate (Rf). The strain recovery rate describes the ability of the material to memorize its permanent shape, while the strain fixity rate describes the ability of switching segments to fix the mechanical deformation.

Result of the cyclic thermomechanical test

whereis the cycle number,is the maximum strain imposed on the material, andandare the strains of the sample in two successive cycles in the stress-free state before yield stress is applied.

Shape-memory effect can be described briefly as the following mathematical model:[8]

whereis the glassy modulus,is the rubbery modulus,is viscous flow strain andis strain for.

Triple-shape memory

edit

While most traditional shape-memory polymers can only hold a permanent and temporary shape, recent technological advances have allowed the introduction of triple-shape-memory materials. Much as a traditional double-shape-memory polymer will change from a temporary shape back to a permanent shape at a particular temperature, triple-shape-memory polymers will switch from one temporary shape to another at the first transition temperature, and then back to the permanent shape at another, higher activation temperature. This is usually achieved by combining two double-shape-memory polymers with different glass transition temperatures[9]or when heating a programmed shape-memory polymer first above the glass transition temperature and then above the melting transition temperature of the switching segment.[10][11]

Description of the thermally induced shape-memory effect

edit
A schematic representation of the shape-memory effect

Polymers exhibiting a shape-memory effect have both a visible, current (temporary) form and a stored (permanent) form. Once the latter has been manufactured by conventional methods, the material is changed into another, temporary form by processing through heating, deformation, and finally, cooling. The polymer maintains this temporary shape until the shape change into the permanent form is activated by a predetermined external stimulus. The secret behind these materials lies in their molecular network structure, which contains at least two separate phases. The phase showing the highest thermal transition,Tperm,is the temperature that must be exceeded to establish the physical crosslinks responsible for the permanent shape. The switching segments, on the other hand, are the segments with the ability to soften past a certain transition temperature (Ttrans) and are responsible for the temporary shape. In some cases this is theglass transition temperature(Tg) and others the melting temperature (Tm). ExceedingTtrans(while remaining belowTperm) activates the switching by softening these switching segments and thereby allowing the material to resume its original (permanent) form. BelowTtrans,flexibility of the segments is at least partly limited. IfTmis chosen for programming the SMP, strain-induced crystallization of the switching segment can be initiated when it is stretched aboveTmand subsequently cooled belowTm.These crystallites form covalent netpoints which prevent the polymer from reforming its usual coiled structure. The hard to soft segment ratio is often between 5/95 and 95/5, but ideally this ratio is between 20/80 and 80/20.[12]The shape-memory polymers are effectively viscoelastic and many models and analysis methods exist.

Thermodynamics of the shape-memory effect

edit

In the amorphous state, polymer chains assume a completely random distribution within the matrix. W represents the probability of a strongly coiled conformation, which is the conformation with maximum entropy, and is the most likely state for an amorphous linear polymer chain. This relationship is represented mathematically byBoltzmann's entropy formulaS=klnW,whereSis theentropyandkis theBoltzmann constant.

In the transition from the glassy state to a rubber-elastic state by thermal activation, the rotations around segment bonds become increasingly unimpeded. This allows chains to assume other possibly, energetically equivalent conformations with a small amount of disentangling. As a result, the majority of SMPs will form compact, random coils because this conformation is entropically favored over a stretched conformation.[1]

Polymers in this elastic state withnumber average molecular weightgreater than 20,000 stretch in the direction of an applied external force. If the force is applied for a short time, the entanglement of polymer chains with their neighbors will prevent large movement of the chain and the sample recovers its original conformation upon removal of the force. If the force is applied for a longer period of time, however, a relaxation process takes place whereby a plastic, irreversible deformation of the sample takes place due to the slipping and disentangling of the polymer chains.[1]

To prevent the slipping and flow of polymer chains, cross-linking can be used, both chemical and physical.

Physically crosslinked SMPs

edit

Linear block copolymers

edit

Representative shape-memory polymers in this category arepolyurethanes,[13][14]polyurethanes with ionic or mesogenic components made byprepolymermethod. Otherblock copolymersalso show the shape-memory effect, such as, block copolymer ofpolyethylene terephthalate(PET) andpolyethyleneoxide(PEO), block copolymers containingpolystyreneand poly(1,4-butadiene), and an ABA triblock copolymer made from poly(2-methyl-2-oxazoline) andpolytetrahydrofuran.

Other thermoplastic polymers

edit

A linear, amorphouspolynorbornene(Norsorex, developed by CdF Chemie/Nippon Zeon) or organic-inorganic hybrid polymers consisting of polynorbornene units that are partially substituted by polyhedral oligosilsesquioxane(POSS) also have shape-memory effect.

Another example reported in the literature is a copolymer consisting of polycyclooctene (PCOE) and poly(5-norbornene-exo,exo-2,3-dicarboxylic anhydride) (PNBEDCA), which was synthesized throughring-opening metathesis polymerization(ROMP). Then the obtained copolymer P(COE-co-NBEDCA) was readily modified by grafting reaction of NBEDCA units with polyhedral oligomeric silsesquioxanes (POSS) to afford a functionalized copolymer P(COE-co-NBEDCA-g-POSS). It exhibits shape-memory effect.[15]

Chemically crosslinked SMPs

edit

The main limitation of physically crosslinked polymers for the shape-memory application is irreversible deformation during memory programming due to thecreep.Thenetwork polymercan be synthesized by either polymerization with multifunctional (3 or more)crosslinkeror by subsequent crosslinking of a linear or branched polymer. They form insoluble materials which swell in certain solvents.[1]

Crosslinked polyurethane

edit

This material can be made by using excess diisocyanate or by using a crosslinker such asglycerin,trimethylol propane.Introduction of covalent crosslinking improves in creep, increase in recovery temperature and recovery window.[16]

PEO based crosslinked SMPs

edit

The PEO-PET blockcopolymerscan be crosslinked by usingmaleic anhydride,glycerin or dimethyl 5-isophthalates as a crosslinking agent. The addition of 1.5 wt% maleic anhydride increased in shape recovery from 35% to 65% and tensile strength from 3 to 5 MPa.[17]

Hard phase Crosslinker Tr(°C) Rf(5)(%) Rf(5)(%)
PET Glycerol/dimethyl 5-sulfoisophthalate 11–30 90–95 60–70
PET Maleic anhydride 8–13 91–93 60
AA/MAA copolymer N,N'-methylene-bis-acrylamide 90 99
MAA/N-vinyl-2-pyrrolidone Ethyleneglycol dimethacrylate 90 99
PMMA/N-vinyl-2-pyrrolidone Ethyleneglycol dimethacrylate 45, 100 99

Thermoplastic shape-memory

edit

While shape-memory effects are traditionally limited tothermosetting plastics,somethermoplasticpolymers, most notablyPEEK,can be used as well.[18]

Light-induced SMPs

edit
A schematic representation of reversible LASMP crosslinking

Light-activated shape-memory polymers (LASMP) use processes of photo-crosslinking and photo-cleaving to changeTg.Photo-crosslinking is achieved by using one wavelength of light, while a second wavelength of light reversibly cleaves the photo-crosslinked bonds. The effect achieved is that the material may be reversibly switched between anelastomerand a rigid polymer. Light does not change the temperature, only the cross-linking density within the material.[19]For example, it has been reported that polymers containing cinnamic groups can be fixed into predetermined shapes byUV lightillumination (> 260 nm) and then recover their original shape when exposed to UV light of a different wavelength (< 260 nm).[19]Examples of photoresponsive switches includecinnamic acidandcinnamylidene acetic acid.

Electro-active SMPs

edit

The use of electricity to activate the shape-memory effect of polymers is desirable for applications where it would not be possible to use heat and is another active area of research. Some current efforts use conducting SMP composites withcarbon nanotubes,[20]short carbon fibers (SCFs),[21][22]carbon black,[23]or metallic Ni powder. These conducting SMPs are produced by chemically surface-modifying multi-walled carbon nanotubes (MWNTs) in a mixed solvent ofnitric acidandsulfuric acid,with the purpose of improving the interfacial bonding between the polymers and the conductive fillers. The shape-memory effect in these types of SMPs have been shown to be dependent on the filler content and the degree of surface modification of the MWNTs, with the surface modified versions exhibiting goodenergy conversion efficiencyand improved mechanical properties.

Another technique being investigated involves the use of surface-modified super-paramagnetic nanoparticles. When introduced into the polymer matrix, remote actuation of shape transitions is possible. An example of this involves the use of oligo (e-caprolactone)dimethacrylate/butyl acrylate composite with between 2 and 12%magnetitenanoparticles.Nickeland hybrid fibers have also been used with some degree of success.[21]

Shape-memory polymers vs. shape-memory alloys

edit
A summary of the major differences between SMPs and SMAs[24]
SMPs SMAs
Density (g/cm3) 0.9–1.2 6–8
Extent of
deformation 		up to 800% <8%
Required stress
for deformation (MPa) 		1–3 50–200
Stress generated
upon recovery (MPa) 		1–3 150–300
Transition
temperatures (°C) 		−10..100 −10..100
Recovery speed 1s –
minutes		 <1s
Processing
conditions 		<200 °C
low
pressure		 >1000 °C
high
pressure
Costs <$10/lb ~$250/lb

Shape-memory polymers differ fromshape memory alloys(SMAs)[25]by their glass transition or melting transition from a hard to a soft phase which is responsible for the shape-memory effect. In shape-memory alloysmartensitic/austenitictransitions are responsible for the shape-memory effect. There are numerous advantages that make SMPs more attractive thanshape memory alloys.They have a high capacity for elastic deformation (up to 200% in most cases), much lower cost, lower density, a broad range of application temperatures which can be tailored, easy processing, potential biocompatibility and biodegradability,[24]and probably exhibit superior mechanical properties to those of SMAs.[26]

Applications

edit

Industrial applications

edit

One of the first conceived industrial applications was in robotics where shape-memory (SM) foams were used to provide initial soft pretension in gripping.[27]These SM foams could be subsequently hardened by cooling, making a shape adaptive grip. Since this time, the materials have seen widespread usage in, for example, the building industry (foam which expands with warmth to seal window frames), sports wear (helmets, judo and karate suits) and in some cases withthermochromicadditives for ease of thermal profile observation.[28]Polyurethane SMPs are also applied as an autochoke element for engines.[29]

Application in photonics

edit

One field in which SMPs are having a significant impact is photonics. Due to the shape changing capability, SMPs enable the production of functional and responsive photonic gratings.[30]By using modern soft lithography techniques such as replica molding, it is possible to imprint periodic nanostructures, with sizes of the order of magnitude of visible light, onto the surface of shape memory polymeric blocks. As a result of the refractive index periodicity, these systems diffract light. By taking advantage of the polymer's shape memory effect, it is possible to reprogram the lattice parameter of the structure and consequently tune its diffractive behavior. Another application of SMPs in photonics is shape changing random lasers.[31]By doping SMPs with highly scattering particles such as titania it is possible to tune the light transport properties of the composite. Additionally, optical gain may be introduced by adding a molecular dye to the material. By configuring both the amount of scatters and of the organic dye, a light amplification regime may be observed when the composites are optically pumped. Shape memory polymers have also been used in conjunction withnanocelluloseto fabricate composites exhibiting both chiroptical properties and thermo-activated shape memory effect.[32]

Medical applications

edit

Most medical applications of SMP have yet to be developed, but devices with SMP are now beginning to hit the market. Recently, this technology has expanded to applications inorthopedic surgery.[18] Additionally, SMPs are now being used in various ophthalmic devices including punctal plugs, glaucoma shunts and intraocular lenses.

Potential medical applications

edit

SMPs aresmart materialswith potential applications as, e.g., intravenous cannula,[29]self-adjusting orthodontic wires and selectively pliable tools for small scale surgical procedures where currently metal-based shape-memory alloys such as Nitinol are widely used. Another application of SMP in the medical field could be its use in implants: for example minimally invasive, through small incisions or natural orifices, implantation of a device in its small temporary shape. Shape-memory technologies have shown great promise for cardiovascular stents, since they allow a small stent to be inserted along a vein or artery and then expanded to prop it open.[33]After activating the shape memory by temperature increase or mechanical stress, it would assume its permanent shape. Certain classes of shape-memory polymers possess an additional property:biodegradability.This offers the option to develop temporary implants. In the case of biodegradable polymers, after the implant has fulfilled its intended use, e.g. healing/tissue regeneration has occurred, the material degrades into substances which can be eliminated by the body. Thus full functionality would be restored without the necessity for a second surgery to remove the implant.[34]Examples of this development are vascularstentsandsurgical sutures.When used in surgical sutures, the shape-memory property of SMPs enables wound closure with self-adjusting optimal tension, which avoids tissue damage due to overtightened sutures and does support healing and regeneration.[35]SMPs have also potential for use ascompression garments[36]and hands-free door openers, whereby the latter can be produced via so-called 4D printing.[37]

Potential industrial applications

edit

Further potential applications include self-repairing structural components, such as e.g. automobile fenders in which dents are repaired by application of temperature.[38]After an undesired deformation, such as a dent in the fender, these materials "remember" their original shape. Heating them activates their "memory". In the example of the dent, the fender could be repaired with a heat source, such as a hair-dryer. The impact results in a temporary form, which changes back to the original form upon heating—in effect, the plastic repairs itself. SMPs may also be useful in the production of aircraft which would morph during flight. Currently, the Defense Advanced Research Projects AgencyDARPAis testing wings which would change shape by 150%.[6]

The realization of a better control over the switching behavior of polymers is seen as key factor to implement new technical concepts. For instance, an accurate setting of the onset temperature of shape recovering can be exploited to tune the release temperature of information stored in a shape memory polymer. This may pave the way for the monitoring of temperature abuses of food or pharmaceuticals.[39]

Recently, a new manufacturing process, mnemosynation, was developed atGeorgia Techto enable mass production of crosslinked SMP devices, which would otherwise be cost-prohibitive using traditional thermoset polymerization techniques.[40]Mnemosynation was named for the Greek goddess of memory,Mnemosyne,and is the controlled imparting of memory on an amorphous thermoplastic materials utilizing radiation-induced covalent crosslinking, much likevulcanizationimparts recoverable elastomeric behavior on rubbers using sulfur crosslinks. Mnemosynation combines advances inionizing radiationand tuning the mechanical properties of SMPs to enable traditional plastics processing (extrusion,blow molding,injection molding,resin transfer molding,etc.) and allows thermoset SMPs in complex geometries. The customizable mechanical properties of traditional SMPs are achievable with high throughput plastics processing techniques to enable mass producible plastic products with thermosetting shape-memory properties: low residual strains, tunable recoverable force and adjustable glass transition temperatures.

Brand protection and anti-counterfeiting

edit

Shape memory polymers may serve as technology platform for a safe way of information storage and release.[41]Overt anti-counterfeiting labels have been constructed that display a visual symbol or code when exposed to specific chemicals.[42]Multifunctional labels may even make counterfeiting increasingly difficult.[43][44]Shape memory polymers have already been made into shape memory film by extruder machine, with covert and overt 3D embossed pattern internally, and 3D pattern will be released to be embossed or disappeared in just seconds irreversibly as soon as it is heated; Shape memory film can be used as label substrates or face stock for anti-counterfeiting,brand protection,tamper-evident seals, anti-pilferage seals, etc.

Multifunctional composites

edit

Using shape memory polymers as matrices, multifunctionalcomposite materialscan be produced. Such composites can have temperature dependant shape morphing (i.e. shape memory) characteristics.[45][46]This phenomenon allows these composites to be potentially used to create deployable structures[47]such as booms,[48]hinges,[49]wings[50][51]etc. While using SMPs can help produce one-way shape morphing structures, it has been reported that using SMPs in combination withshape memory alloysallows creation of more complex shape memory composites that is capable of two-way shape memory deformation.[52]

See also

edit

References

edit
  1. ^abcdLendlein, A., Kelch, S. (2002). "Shape-memory polymers".Angew. Chem. Int. Ed.41(12): 2034–2057.doi:10.1002/1521-3773(20020617)41:12<2034::AID-ANIE2034>3.0.CO;2-M.PMID19746597.S2CID35309743.{{cite journal}}:CS1 maint: multiple names: authors list (link)
  2. ^Horie, K.; Barón, Máximo; Fox, R. B.; He, J.; Hess, M.; Kahovec, J.; Kitayama, T.; Kubisa, P.; Maréchal, E.; Mormann, W.; Stepto, R. F. T.; Tabak, D.; Vohlídal, J.; Wilks, E. S.; Work, W. J. (1 January 2004)."Definitions of terms relating to reactions of polymers and to functional polymeric materials (IUPAC Recommendations 2003)".Pure and Applied Chemistry.76(4): 889–906.doi:10.1351/pac200476040889.S2CID98351038.
  3. ^Mohr, R.; Kratz, K.; Weigel, T.; Lucka-Gabor, M.; Moneke, M.; Lendlein, A. (2006)."Initiation of shape-memory effect by inductive heating of magnetic nanoparticles in thermoplastic polymers".Proceedings of the National Academy of Sciences.103(10): 3540–5.Bibcode:2006PNAS..103.3540M.doi:10.1073/pnas.0600079103.PMC1383650.PMID16537442.
  4. ^Lendlein, A.; Jiang, H.; Jünger, O.; Langer, R. (2005). "Light-induced shape-memory polymers".Nature.434(7035): 879–82.Bibcode:2005Natur.434..879L.doi:10.1038/nature03496.PMID15829960.S2CID4391911.
  5. ^Leng, J.; Lv, H.; Liu, Y.; Du, S. (2008)."Comment on" Water-driven programable [sic] polyurethane shape memory polymer: Demonstration and mechanism "[Appl. Phys. Lett. 86, 114105 (2005)]".Applied Physics Letters.92(20): 206105.doi:10.1063/1.2936288.
  6. ^abToensmeier, P.A. (2 April 2009)"Shape memory polymers reshape product design",Plastics Engineering.
  7. ^Voit, W.; Ware, T.; Dasari, R. R.; Smith, P.; Danz, L.; Simon, D.; Barlow, S.; Marder, S. R.; Gall, K. (2010). "High-Strain Shape-Memory Polymers".Advanced Functional Materials.20:162–171.doi:10.1002/adfm.200901409.S2CID97133730.
  8. ^Kim B.K.; Lee S.Y.; Xu M. (1996). "Polyurethanes having shape memory effects".Polymer.37(26): 5781.doi:10.1016/S0032-3861(96)00442-9.
  9. ^Bellin, I.; Kelch, S.; Langer, R.; Lendlein, A. (2006)."Polymeric triple-shape materials".Proceedings of the National Academy of Sciences.103(48): 18043–7.Bibcode:2006PNAS..10318043B.doi:10.1073/pnas.0608586103.PMC1838703.PMID17116879.
  10. ^Pretsch, T. (2010). "Triple-shape properties of a thermoresponsive poly(ester urethane)".Smart Materials and Structures.19(1): 015006.Bibcode:2010SMaS...19a5006P.doi:10.1088/0964-1726/19/1/015006.S2CID135951371.
  11. ^Bothe, M., Mya, K. Y., Lin, E. M. J., Yeo, C. C., Lu, X., He, C., Pretsch, T. (2012). "Triple-shape properties of star-shaped POSS-polycaprolactone polyurethane networks".Soft Matter.8(4): 965–972.Bibcode:2012SMat....8..965B.doi:10.1039/C1SM06474F.{{cite journal}}:CS1 maint: multiple names: authors list (link)
  12. ^Shanmugasundaram, O.L. (2009)."Shape Memory Polymers & their applications".The Indian Textile Journal.
  13. ^Chan, B. Q. Y.; Liow, S. S.; Loh, X. J. (2016). "Organic–inorganic shape memory thermoplastic polyurethane based on polycaprolactone and polydimethylsiloxane".RSC Adv.6(41): 34946–34954.Bibcode:2016RSCAd...634946C.doi:10.1039/C6RA04041A.
  14. ^Chan, B. Q. Y.; Heng, S. J. W.; Liow, S. S.; Zhang, K.; Loh, X. J. (2017). "Dual-responsive hybrid thermoplastic shape memory polyurethane".Mater. Chem. Front.1(4): 767–779.doi:10.1039/C6QM00243A.
  15. ^Dan Yanga, Danyi Gaoa, Chi Zenga, Jisen Jiangb, Meiran Xie (2011). "POSS-enhanced shape-memory copolymer of polynorbornene derivate and polycyclooctene through ring-opening metathesis polymerization".Reactive and Functional Polymers.71(11): 1096–1101.doi:10.1016/j.reactfunctpolym.2011.08.009.{{cite journal}}:CS1 maint: multiple names: authors list (link)
  16. ^Buckley CP.; Prisacariu C.; Caraculacu A. (2007). "Novel triol-crosslinked polyurethanes and their thermorheological characterization as shape-memory materials".Polymer.48(5): 1388.doi:10.1016/j.polymer.2006.12.051.
  17. ^Park, C.; Yul Lee, J.; Chul Chun, B.; Chung, Y. C.; Whan Cho, J.; Gyoo Cho, B. (2004). "Shape memory effect of poly(ethylene terephthalate) and poly(ethylene glycol) copolymer cross-linked with glycerol and sulfoisophthalate group and its application to impact-absorbing composite material".Journal of Applied Polymer Science.94:308–316.doi:10.1002/app.20903.
  18. ^abAnonymous."Surgical Technologies; MedShape Solutions, Inc. Announces First FDA-cleared Shape Memory PEEK Device; Closing of $10M Equity Offering".Medical Letter on the CDC & FDA.
  19. ^abHavens, E.; Snyder, E.A.; Tong, T.H. (2005). White, Edward V (ed.). "Light-activated shape memory polymers and associated applications".Proc. SPIE.Smart Structures and Materials 2005: Industrial and Commercial Applications of Smart Structures Technologies.5762:48.Bibcode:2005SPIE.5762...48H.doi:10.1117/12.606109.S2CID136939515.
  20. ^Liu, Y.; Lv, H.; Lan, X.; Leng, J.; Du, S. (2009). "Review of electro-active shape-memory polymer composite".Composites Science and Technology.69(13): 2064.doi:10.1016/j.compscitech.2008.08.016.
  21. ^abLeng, J.; Lv, H.; Liu, Y.; Du, S. (2007). "Electroactivate shape-memory polymer filled with nanocarbon particles and short carbon fibers".Applied Physics Letters.91(14): 144105.Bibcode:2007ApPhL..91n4105L.doi:10.1063/1.2790497.
  22. ^Leng, J.; Lv, H.; Liu, Y.; Du, S. (2008). "Synergic effect of carbon black and short carbon fiber on shape memory polymer actuation by electricity".Journal of Applied Physics.104(10): 104917–104917–4.Bibcode:2008JAP...104j4917L.doi:10.1063/1.3026724.
  23. ^Kai, D.; Tan, M. J.; Prabhakaran, M. P.; Chan, B. Q. Y.; Liow, S. S.; Ramakrishna, S.; Loh, X. J. (1 December 2016). "Biocompatible electrically conductive nanofibers from inorganic-organic shape memory polymers".Colloids and Surfaces B: Biointerfaces.148:557–565.doi:10.1016/j.colsurfb.2016.09.035.PMID27690245.
  24. ^abLiu, C.; Qin, H.; Mather, P. T. (2007). "Review of progress in shape-memory polymers".Journal of Materials Chemistry.17(16): 1543.CiteSeerX10.1.1.662.758.doi:10.1039/b615954k.S2CID138860847.
  25. ^Czichos H. (1989) "Adolf Martens and the Research on Martensite", pp. 3–14 inThe Martensitic Transformation in Science and TechnologyE. Hornbogen and N. Jost (eds. ). Informationsgesellschaft.ISBN3883551538.
  26. ^Jani, J. M.; Leary, M.; Subic, A.; Gibson, M. A. (2013). "A Review of Shape Memory Alloy Research, Applications and Opportunities".Materials & Design.56:1078–1113.doi:10.1016/j.matdes.2013.11.084.S2CID108440671.
  27. ^Brennan, Mairin (2001)."Suite of shape-memory polymers".Chemical and Engineering News.79(6): 5.doi:10.1021/cen-v079n006.p005.
  28. ^Monkman. G.J. and Taylor, P.M. (June 1991) "Memory Foams for Robot Grippers Robots in Unstructured Environments", pp. 339–342 inProc. 5th Intl. Conf. on Advanced Robotics,Pisa.
  29. ^abTobushi, H.; Hayashi, S.; Hoshio, K.; Ejiri, Y. (2008)."Shape recovery and irrecoverable strain control in polyurethane shape-memory polymer".Science and Technology of Advanced Materials.9(1): 015009.Bibcode:2008STAdM...9a5009T.doi:10.1088/1468-6996/9/1/015009.PMC5099815.PMID27877946.
  30. ^Espinha, A.; Serrano, M. C.; Blanco, A.; López, C. (2014). "Thermoresponsive shape-memory photonic nanostructures".Advanced Optical Materials.2(6): 516.doi:10.1002/adom.201300532.S2CID96675130.
  31. ^Espinha, A.; Serrano, M. C.; Blanco, A.; López, C. (2015). "Random lasing in novel dye-doped white paints with shape memory".Advanced Optical Materials.3(8): 1080.doi:10.1002/adom.201500128.S2CID95962110.
  32. ^Espinha, André; Guidetti, Giulia; Serrano, María C; Frka-Petesic, Bruno; Dumanli, Ahu Gümrah; Hamad, Wadood Y; Blanco, Álvaro; López, Cefe; Vignolini, Silvia (8 November 2016)."Shape memory cellulose-based photonic reflectors".ACS Applied Materials & Interfaces.8(46): 31935–31940.doi:10.1021/acsami.6b10611.PMC5495156.PMID27786436.
  33. ^Yakacki, C. M.; Shandas, R.; Lanning, C.; Rech, B.; Eckstein, A.; Gall, K. (2007)."Unconstrained recovery characterization of shape-memory polymer networks for cardiovascular applications".Biomaterials.28(14): 2255–63.doi:10.1016/j.biomaterials.2007.01.030.PMC2700024.PMID17296222.
  34. ^Chan, B. Q. Y.; Low, Z. W. K.; Heng, S. J. W.; Chan, S. Y.; Owh, C.; Loh, X. J. (27 April 2016). "Recent Advances in Shape Memory Soft Materials for Biomedical Applications".ACS Applied Materials & Interfaces.8(16): 10070–10087.doi:10.1021/acsami.6b01295.PMID27018814.
  35. ^Lendlein, A., Langer, R. (2002)."Biodegradable, Elastic Shape Memory Polymers for Potential Biomedical Applications".Science.296(5573): 1673–1675.Bibcode:2002Sci...296.1673L.doi:10.1126/science.1066102.PMID11976407.S2CID21801034.{{cite journal}}:CS1 maint: multiple names: authors list (link)
  36. ^Tonndorf, R.; Aibibu, D.; Cherif, C. (2020)."Thermoresponsive Shape Memory Fibers for Compression Garments".Polymers.12(12): 2989.doi:10.3390/polym12122989.ISSN2073-4360.PMC7765188.PMID33333755.
  37. ^Chalissery, Dilip; Schönfeld, Dennis; Walter, Mario; Shklyar, Inga; Andrae, Heiko; Schwörer, Christoph; Amann, Tobias; Weisheit, Linda; Pretsch, Thorsten (2022)."Highly Shrinkable Objects as Obtained from 4D Printing".Macromolecular Materials and Engineering.307:2100619.doi:10.1002/mame.202100619.ISSN1439-2054.S2CID244178629.
  38. ^Monkman. G.J. (June–August 2000). "Advances in Shape Memory Polymer Actuation".Mechatronics.10(4/5): 489–498.doi:10.1016/S0957-4158(99)00068-9.
  39. ^Fritzsche, N., Pretsch, T. (2014). "Programming of Temperature-Memory Onsets in a Semicrystalline Polyurethane Elastomer".Macromolecules.47(17): 5952–5959.Bibcode:2014MaMol..47.5952F.doi:10.1021/ma501171p.{{cite journal}}:CS1 maint: multiple names: authors list (link)
  40. ^Voit, W.; Ware, T.; Gall, K. (2010). "Radiation crosslinked shape-memory polymers".Polymer.51(15): 3551.doi:10.1016/j.polymer.2010.05.049.
  41. ^Pretsch, T., Ecker, M., Schildhauer, M., Maskos, M. (2012). "Switchable information carriers based on shape memory polymer".Journal of Materials Chemistry.22(16): 1673–1675.doi:10.1039/C2JM16204K.{{cite journal}}:CS1 maint: multiple names: authors list (link)
  42. ^Leverant, Calen J.; Leo, Sin-Yen; Cordoba, Maria A.; Zhang, Yifan; Charpota, Nilesh; Taylor, Curtis; Jiang, Peng (11 January 2019). "Reconfigurable Anticounterfeiting Coatings Enabled by Macroporous Shape Memory Polymers".ACS Applied Polymer Materials.1(1): 36–46.doi:10.1021/acsapm.8b00021.S2CID139393495.
  43. ^Ecker, M., Pretsch, T. (2014). "Multifunctional poly(ester urethane) laminates with encoded information".RSC Advances.4(1): 286–292.Bibcode:2014RSCAd...4..286E.doi:10.1039/C3RA45651J.{{cite journal}}:CS1 maint: multiple names: authors list (link)
  44. ^Ecker, M., Pretsch, T. (2014)."Novel design approaches for multifunctional information carriers".RSC Advances.4(87): 46680–46688.Bibcode:2014RSCAd...446680E.doi:10.1039/C4RA08977D.{{cite journal}}:CS1 maint: multiple names: authors list (link)
  45. ^Chan, Benjamin Qi Yu; Chong, Yi Ting; Wang, Shengqin; Lee, Coryl Jing Jun; Owh, Cally; Wang, Fei; Wang, FuKe (February 2022)."Synergistic combination of 4D printing and electroless metallic plating for the fabrication of a highly conductive electrical device".Chemical Engineering Journal.430:132513.doi:10.1016/j.cej.2021.132513.S2CID240565520.
  46. ^Chen, Yijin; Sun, Jian; Liu, Yanju; Leng, Jinsong (1 September 2012)."Variable stiffness property study on shape memory polymer composite tube".Smart Materials and Structures.21(9): 094021.Bibcode:2012SMaS...21i4021C.doi:10.1088/0964-1726/21/9/094021.ISSN0964-1726.S2CID137128745.
  47. ^Arzberger, Steven C.; Tupper, Michael L.; Lake, Mark S.; Barrett, Rory; Mallick, Kaushik; Hazelton, Craig; Francis, William; Keller, Phillip N.; Campbell, Douglas; Feucht, Sara; Codell, Dana (5 May 2005). White, Edward V (ed.)."Elastic memory composites (EMC) for deployable industrial and commercial applications".Smart Structures and Materials 2005: Industrial and Commercial Applications of Smart Structures Technologies.5762.SPIE: 35–47.Bibcode:2005SPIE.5762...35A.doi:10.1117/12.600583.S2CID137216745.
  48. ^Puig, L.; Barton, A.; Rando, N. (1 July 2010)."A review on large deployable structures for astrophysics missions".Acta Astronautica.67(1): 12–26.Bibcode:2010AcAau..67...12P.doi:10.1016/j.actaastro.2010.02.021.ISSN0094-5765.
  49. ^Lan, Xin; Liu, Yanju; Lv, Haibao; Wang, Xiaohua; Leng, Jinsong; Du, Shanyi (20 January 2009)."Fiber reinforced shape-memory polymer composite and its application in a deployable hinge".Smart Materials and Structures.18(2): 024002.Bibcode:2009SMaS...18b4002L.doi:10.1088/0964-1726/18/2/024002.ISSN0964-1726.S2CID135594892.
  50. ^Rodriguez, Armando (8 January 2007),"Morphing Aircraft Technology Survey",45th AIAA Aerospace Sciences Meeting and Exhibit,Aerospace Sciences Meetings, American Institute of Aeronautics and Astronautics,doi:10.2514/6.2007-1258,ISBN978-1-62410-012-3,retrieved1 December2021
  51. ^Yu, Kai; Sun, Shouhua; Liu, Liwu; Zhang, Zhen; Liu, Yanju; Leng, Jinsong (20 October 2009)."Novel deployable morphing wing based on SMP composite".In Leng, Jinsong; Asundi, Anand K; Ecke, Wolfgang (eds.).Second International Conference on Smart Materials and Nanotechnology in Engineering.Vol. 7493. SPIE. pp. 708–714.Bibcode:2009SPIE.7493E..2JY.doi:10.1117/12.845408.S2CID110298351.
  52. ^Tobushi, Hisaaki; Hayashi, Shunichi; Sugimoto, Y.; Date, K. (January 2010)."Fabrication and Two-Way Deformation of Shape Memory Composite with SMA and SMP".Materials Science Forum.638–642: 2189–2194.doi:10.4028/www.scientific.net/MSF.638-642.2189.ISSN1662-9752.S2CID137480356.
Retrieved from "https://en.wikipedia.org/w/index.php?title=Shape-memory_polymer&oldid=1246366169"